Haynes 556 Nickel Alloy
Haynes 556 (tsis ntseeg (UNSIVAL R30556) yog hom hlau- ribt {}}} kub}} kub lub zog thiab oxidation tsis kam. Nws tuaj yeem ua kom tau zoo sulfidation, carburization, thiab corrosion, thiab corrosion nyob rau hauv chlorine {} li yaig los ntawm molten salts thiab zinc. Nws zoo heev machining ua kom nws dav siv nyob rau hauv ib puag ncig heev xws li cov tshuab cua tshuab, cov khib nyiab, thiab cov khoom siv tshuaj che.
Tshuaj Muaj Tshuaj
| C | Si | Mn | P | S | Cr | Ni | Mo | N | W | Tsaus yr | B | Co las | Al | Ta | Tsheb hauv paus | Lauj kaub | Zaum fe | |
| Lub min | 0.05 | 0.2 | 0.5 | - | - | 21 | 19 | 2.5 | 0.1 | 2 | 0.001 | - | 16 | 0.1 | 0.3 | - | 0.005 | Ntxiv |
| Tus zuag | 0.15 | 0.8 | 2 | 0.04 | 0.015 | 23 | 22.5 | 4 | 0.3 | 3.5 | 0.1 | 0.02 | 21 | 0.5 | 1.25 | 0.3 | 0.1 |
Khoom Siv Khoom
|
Ceev |
Melting point |
Yam tsawg kawg nkaus cov cuab yeej cuab tam ntawm cov alloy ntawm chav tsev kub |
||
|
Lub zog tensile |
Paib lub zog |
Elongation |
||
|
g / cm3 |
tiv kis |
RM N / MM2 |
Rp0.2 n / mm2 |
A5% |
|
8.23 |
1330-1415 |
793 |
379 |
40 |
Tus qauv
ASTM B572, ASTM B446, AMS 5536
Yam zoo
Haynes 556: resistacts sulfidation, chlorine corrosion, molten salts / zinc; Lub zog siab / cov txheej txheem; Cov Khoom Siv Hluav Taws Xob Zoo Tshaj Rau Ni / Co / Fe - Raws li alloys
Cov Ntawv Thov
Corrosion-intensive systems: Waste incinerators, rotary calciners, hot-dip galvanizing, aerospace hot-section parts
Cim npe nrov: Haynes 556 Nickel Alloy, Tuam Tshoj Haynes 556 Nickel Alloy Manufacturers, Chaw muag khoom, Hoobkas